Description
ASI Torque 03 RC Retaining compound is engineered to greatly increase the shear strength of cylindrical, non-threaded assemblies, by filling the inner space and surface irregularities between parts forming a tough, durable polymer. Torque 03 RC is a high-strength anaerobic adhesive for retaining of close-fitted parts, shafts, bushes, pulleys, and rotors. Can be used on oily surfaces. Resistant to heat, corrosion and vibration.
Product | Color | Viscosity | Gap Fill | Shear Strength Steel/Steel |
Temp Range | Cure Speed (Fixture/Full) |
Specific Gravity |
Torque 03 RC Excellent for oily surfaces and other contamination. Prevents corrosion, provides strength up to 3,800 psi, temperature resistance to 350°F MIL-R-46082B, Type I |
Green | 125 cps | .005″ | 3,800 psi | -65 TO 350°F | 10 Min/8 Hours | 1.100 |
Torque 09 RC General purpose, low viscosity retaining compound. Fixtures in under 10 minutes, providing shear strength up to 3,800 psi, works well on similar an dissimilar metals. Temperature resistant to 350°F. MIL-R-46082B, Type I |
Green | 125 cps | .005″ | 3,800 psi | -65 TO 350°F | 15 Min/8 Hours | 1.100 |
Torque 20 RC High strength, high temperature retaining compound. Shear strength up to 4,000 psi, radial clearance up to .015″. Fixtures in under 15 minutes. |
Green | 8,500 cps | .015″ | 4,000 psi | -65 TO 450°F | 15 Min/8 Hours | 1.160 |
Torque 35 RC Medium viscosity, ideal for slip fitted parts. Fixtures in 10 minutes, shear strength up to 4,200 psi, temperature up to 350°F MIL-R-46082B, Type III |
Green | 2,000 cps | .010″ | 4,200 psi | -65 TO 350°F | 10 Min/8 Hours | 1.050 |
Torque 38 RC Maximum strength for extremely high dynamic loading. 4,500 psi in shear strength, radial clearance up to .010″. |
Green | 2,500 cps | .010″ | 4,500 psi | -65 TO 350°F | 2 Min/8 Hours | 1.019 |
Torque 40 RC Medium strength, delayed curing for maximum adjustment times, up to 40 minutes. High temperature up to 450°F. MIL-R-46082B, Type II |
Green | 600 cps | .007″ | 3,500 psi | -65 TO 450°F | 40 Min/8 Hours | 1.120 |
Torque 41 RC General purpose, controlled strength retaining. Excellent for parts that require disassembly. Radial clearance up to .010″. |
Yellow | 750 cps | .010″ | 1,800 psi | -65 TO 350°F | 15 Min/8 Hours | 1.070 |
Torque 48 RC Fast curing, high strength. Working temperatures up to 350°F. Fixtures in under 2 minutes. |
Green | 500 cps | .006″ | 4,000 psi | -65 TO 350°F | 2 Min/8 Hours | 1.130 |
Torque 60 RC Repair compound for worn threads and/or machine parts. Restores parts to correct tolerances. Fills gaps up to .020″. |
Silver | 250,000 cps | .020″ | 3,500 psi | -65 TO 350°F | 10 Min/24 Hours | 1.130 |
Torque 75 RC Low viscosity, delayed curing up to 30 minutes for positioning and adjustment. Ideal for press fib. MIL-R-46082B, Type I |
Green | 125 cps | .005″ | 3,500 psi | -65 TO 350°F | 30 Min/24 Hours | 1.090 |
Torque 80 RC High strength for slip fitted parts, 4,200 psi. Fixtures in under 5 minutes with gap filling up to .015″. |
Green | 1,400 cps | .015″ | 4,200 [si | -65 TO 350°F | 5 Min/8 Hours | 1.110 |
About the ASI TORQUE RC Series Retaining Compounds
The TORQUE RETAINING SERIES is engineered to greatly increase the shear strength of cylindrical, non threaded assemblies. These products fill the inner space and surface irregularities between the parts forming a tough, durable polymer, that creates a unitized, strong, precision assembly, preventing corrosion. They are single component, solvent free compounds that are ready to use right from the bottle, or can be easily automated. The TORQUE RETAINING SERIES is formulated in a wide range of viscosities, gap filling ability, cure times and strength characteristics. This technology greatly enhances the reliability and performance properties of the finished assembly. Even in the best press fit application there is only 20 to 30 percent actual metal contact between the surfaces.
The TORQUE RETAINING SERIES fills all the voids between the parts increasing the overall strength of the assembly by 2 to 3 times that of the original press fit. Other retaining and locking devices can be eliminated such as keyways, set screws, splines, tapers, knurls, etc. Machining tolerances can be relaxed lowering the cost of the assembly and simplifying the assembly process. Improved quality, reliability, cost effectiveness, ease of use, are just a few of the many benefits the TORQUE RETAINING SERIES brings to improve the manufacturing techniques in your assembly applications.